Brazing alloy L-CuZn40 according to DIN EN 1044

L-CuZn40 according to DIN EN 1044, B-Cu60Zn(Si)(Mn)-870/900 according to DIN EN ISO 3677
Form: Rods of 2x500 mm
Working temperature: 900 °C
Unit weight: approx. 13 g
Tensile strength: 300-400 N/mm²
Can be used for soldering copper, iron, steel and nickel alloys

Price range: 7,99 € through 72,99 € inkl. MwSt.

Combination

Clear

EAN: 4255797344721 SKU: L-CuZn40-XXXX-XXX Categories: Alloys, Brazing Alloys Tags: Brazing, Copper Pipes, FH10

Description

L-CuZn40, BRASS 60, CU 303 according to DIN EN 1044, B-Cu60Zn(Si)(Mn)-870/900 according to DIN EN ISO 3677

Composition: 61.5 – 58.5 % copper, 37.85 – 41.3 % zinc, 0.05 – 0.25 % manganese and 0.15 – 0.4 % silicon
Form: Round rods of 2×500 mm
Unit weight: approx. 13 g
Working temperature: 900 °C
Melting range: 870 – 900 °C
Density: 8.4 g/cm³
Tensile strength: 300 – 400 N/mm²
Brinell hardness (HB): 110
Elongation at break: 30 %

The brazing alloy L-CuZn40 is a common copper/brass brazing alloy and is preferably used to braze copper alloys with a solidus temperature above 950 °C, unalloyed or low-alloy steels, as well as nickel and nickel alloys.

Fluxes based on FH21 and FH10 can be used during the soldering process. Since FH10, unlike FH21, is freely available because it contains more compatible substances, we recommend using this flux for brazing L-CuZn40.

For a quantity of up to 5 pieces, we offer the rods divided in the middle in order to be able to provide you with a more favorable price by saving on shipping costs.